Development, physicochemical characterization and in-vitro biocompatibility study of dromedary camel dentine derived hydroxyapatite for bone repair.

This study aimed to produce hydroxyapatite from the dentine portion of camel teeth using a defatting and deproteinizing procedure and characterize its physicochemical and biocompatibility properties. Biowaste such as waste camel teeth is a valuable source of hydroxyapatite, the main inorganic constituent of human bone and teeth which is frequently used as bone grafts in the biomedical field. Fourier Transform infrared (FTIR), and micro-Raman spectroscopy confirmed the functional groups as-sociated with hydroxyapatite. X-ray diffraction (XRD) studies showed camel dentine-derived hydroxyapatite (CDHA) corresponded with hydroxyapatite spectra. Scanning electron micros-copy (SEM) demonstrated the presence of dentinal tubules measuring from 1.69-2.91 µm. The inorganic phases of CDHA were primarily constituted of calcium and phosphorus, with trace levels of sodium, magnesium, potassium, and strontium, according to energy dispersive X-ray analysis (EDX) and inductively coupled plasma mass spectrometry (ICP-MS). After 28 days of incubation in simulated body fluid (SBF), the pH of the CDHA scaffold elevated to 9.2. in-vitro biocompatibility studies showed that the CDHA enabled Saos-2 cells to proliferate and express the bone marker osteonectin after 14 days of culture. For applications such as bone augmentation and filling bone gaps, CDHA offers a promising material. However, to evaluate the clinical feasibility of the CDHA, further in-vivo studies are required.

Extraction of Hydroxyapatite from Camel Bone for Bone Tissue Engineering Application.

Waste tissues such as mammalian bone are a valuable source from which to extract hydroxyapatite. Camel bone-based hydroxyapatite (CBHA) was extracted from the femur of camel bones using a defatting and deproteinization procedure. The extracted CBHA was mechanically, chemically, physically, morphologically and structurally characterized. Fourier-Transform Infra-Red (FTIR) spectra, Micro-Raman, and X-ray diffraction analysis confirmed successful extraction of hydroxyapatite. The mechanical properties of the CBHA scaffold were measured using a Universal Instron compression tester. Scanning electron microscopy showed the presence of a characteristic interconnected porous architecture with pore diameter ranging from 50-600 µm and micro-computer tomography (Micro-CT) analysis identified a mean porosity of 73.93. Thermogravimetric analysis showed that the CBHA was stable up to 1000 °C and lost only 1.435% of its weight. Inductively coupled plasma-mass spectrometry (ICP-MS) and Energy-dispersive-X-ray (EDX) analysis demonstrated the presence of significant amounts of calcium and phosphorus and trace ions of sodium, magnesium, zinc, lead and strontium. Following 21 days of incubation in simulated body fluid (SBF), the pH fluctuated between 10-10.45 and a gradual increase in weight loss was observed. In conclusion, the extracted CBHA is a promising material for future use in bone tissue regeneration applications.